Process for purifying molybdenum

ABSTRACT

A process is disclosed for purifying molybdenum containing arsenic and phosphorus which involves leaching molybdenum trioxide in an acid at a temperature of above about 70° C. to remove impurities from the molybdenum trioxide and produce a partially purified molybdenum trioxide, adding to an acidic slurry of the leached molybdenum trioxide, a source of magnesium ions in a solid form with the amount of magnesium and the magnesium ion concentration in the subsequently formed ammonium molybdate solution being sufficient to subsequently form insoluble material containing greater than about 80% by weight of the arsenic and greater than about 80% by weight of the phosphorus, and ammonia in an amount sufficient to subsequently dissolve the molybdenum and subsequently form the insoluble material, digesting the resulting ammoniated slurry at a temperature sufficient to dissolve the molybdenum and form an ammonium molybdate solution while the pH is maintained at from about 9 to about 10 to form the insoluble material wherein the arsenic is present as magnesium ammonium arsenate and the phosphorus is present as magnesium ammonium phosphate, and separating the insoluble material from the ammonium molybdate solution.

This application is a continuation-in-part of application Ser. No. 099,266, filed Sept. 21, 1987 and assigned to the same assignee as the present application.

This invention relates to a process for purifying molybdenum. More particularly, it relates to a process for purifying molybdenum of the impurities of arsenic and phosphorus by adding magnesium ions to a slurry of molybdenum trioxide, either before or after addition of ammonia to produce insoluble material containing arsenic and phosphorus.

BACKGROUND OF THE INVENTION

Sources of molybdenum such as impure or technical grade molybdenum trioxide are often contaminated with phosphorus and/or arsenic. These impurities are difficult to remove and are often present as contaminants in molybdenum compounds where they result in inferior quality of molybdenum products. For example, phosphorus in ammonium dimolybdate shows up in the subsequently produced molybdenum metal. Phosphorus at a level of about 40 ppm in molybdenum powder causes a decrease in the rolling efficiency of molybdenum.

Therefore a method to remove impurities such as phosphorus and arsenic from molybdenum would be advantageous because it would allow processing of a wide variety of molybdenum sources.

U.S. Pat. No. 3,829,550 discloses a process for producing a high purity molybdenum trioxide and/or ammonium molybdate product whereby an oxidized molybdenite concentrate is subjected to an ammonium hydroxide leaching step including a digestion phase in which an oxidation of some of the impurities therein, particularly iron, is effected, resulting in a coprecipitation of iron and aluminum hydroxide, together with other impurities including lead, bismuth, tin, arsenic, phosphorus, soluble silica, and the like. The resultant aqueous solution containing ammonium molybdate is filtered and thereafter crystallized, followed by calcining to produce a high purity molybdenum trioxide. This molybdenum trioxide can be further purified by digestion in dilute nitric acid solution to effect a further leaching of residual contaminants, and thereafter the molybdenum trioxide is redissolved in an aqueous ammonium hydroxide solution which is filtered and subsequently crystallized to produce a high purity ammonium molybdate.

U.S. Pat. No. 4,273,745 relates to a process for recovering molybdenum from ammonium molybdate solution containing phosphate ions by digesting in an ammonium molybdate solution at least one water soluble compound of aluminum, calcium, iron or magnesium to precipitate phosphate, and thereafter processing the molybdenum to produce ammonium polymolybdate. Removal of arsenic with magnesium is not discussed in this patent.

U.S. Pat. Nos. 4,278,644 and 4,298,582 relate to processes for recovering chromium, vanadium, molybdenum, and tungsten from secondary resources such as alloy scrap comprising a refractory metal and base metals such as cobalt, nickel, iron, and copper. There is a phosphorus removal step. However, the ammonia content is far below that of the present invention. Furthermore, the phosphorus is reduced to less than 0.02 g P/l. The present invention starts with less than this.

U.S. Pat. No. 4,320,094 relates to recovery of refractory and base metals from superalloy scrap. It provides a solution suitable for subsequent hydrometallurgical recovery of the metals. This patent teaches removal of phosphate from alkaline alkali metal solution.

SUMMARY OF THE INVENTION

In accordance with one aspect of this invention, there is provided a process for purifying molybdenum containing arsenic and phosphorus which involves leaching molybdenum trioxide in an acid at a temperature of above about 70° C. to remove impurities from the molybdenum trioxide and produce a partially purified molybdenum trioxide, adding to an acidic slurry of the leached molybdenum trioxide a source of magnesium ions in a solid form with the amount of magnesium and the magnesium ion concentration in the subsequently formed ammonium molybdate solution being sufficient to subsequently form insoluble material containing greater than about 80% by weight of the arsenic and greater than about 80% by weight of the phosphorus, and ammonia in an amount sufficient to subsequently dissolve the molybdenum and subsequently form the insoluble material, digesting the resulting ammoniated slurry at a temperature sufficient to dissolve the molybdenum and form an ammonium molybdate solution while the pH is maintained at from about 9 to about 10 to form insoluble material wherein the arsenic is present as magnesium ammonium arsenate and the phosphorus is present as magnesium ammonium phosphate, and separating the insoluble material from the ammonium molybdate solution.

DETAILED DESCRIPTION OF THE INVENTION

For a better understanding of the present invention, together with other and further objects, advantages and capabilities thereof, reference is made to the following disclosure and appended claims in connection with the above description of some of the aspects of the invention.

The invention provides a process for removing arsenic and phosphorus from molybdenum by precipitation of insoluble magnesium ammonium compounds of arsenic and phosphorus from ammonium molybdate solution. The advantage of the present invention is that addition of the magnesium ion is incorporated into the process for producing ammoniacal molybdenum compounds from impure molybdenum trioxide by being added directly to the starting molybdenum trioxide slurry, in contrast with prior art techniques of adding the magnesium source as a separate step to the ammonium molybdate solution thus formed. In this way, an extra processing step is saved along with cost savings.

The starting molybdenum of this invention is molybdenum trioxide most typically in the impure form such as technical grade material. Most typically the molybdenum trioxide contains from about 1 to about 100 weight parts per million (ppm) phosphous and from about 1 to about 120 weight ppm of arsenic.

The molybdenum trioxide is leached in an acid to remove some impurities, especially at least some iron and aluminum. In this treatment, the molybdenum trioxide is acid leached at a temperature of above about 70° C. and preferably from about 75° C. to about 85° C. for a length of time of preferably from about 2 hours to about 21/2 hours. Most preferably a nitric acid system is used which is most typically about 2 molar in nitric acid. The bulk of the acid is then removed from the molybdenum ususally by being decanted off. The acid leached molybdenum is then water washed most typically by being slurried with water one or more times. This is done most typically at about 60° C. for about 30 minutes for each separate wash. The wash water is then removed usually by filtration or decantation from molybdenum trioxide after the trioxide has been allowed to settle. In accordance with a preferred embodiment, water is then added to the washed molybdenum trioxide. This acid slurry can be used as the acidic slurry of the next step of the present invention.

Although the above has been described as a preferred method of obtaining the acidic molybdenum slurry, it is to be understood that an acid slurry of the molybdenum trioxide can be formed in any way.

An oxidizing agent can be added to this slurry. Most typically the oxidizing agent is hydrogen peroxide. This is done to insure that the Mo and any Fe present are in their highest oxidation states which is advantageous in further processing steps.

A source of magnesium ions is added to this slurry with the amount of magnesium being sufficient to subsequently form insoluble material which contains the major portion of any arsenic and phosphorus which are present. Some preferred sources of magnesium ions are magnesium oxide, magnesium hydroxide, magnesium carbonate, magnesium nitrate, magnesium chloride, magnesium sulfate, and combinations of these. It is preferred to have the source of magnesium from the first three becuase there is no contamination from anions. The amount of magnesium is typically sufficient to result in a magnesium concentration of from about 0.005 to about 0.04 moles Mg/l in the molybdate solution. The amount of magnesium ions and the magnesium ion concentration in the subsequently formed ammonium molybdate solution is sufficient to subsequently form insoluble material containing greater than about 80% by weight of the arsenic and greater than about 80% by weight of the phosphorus which may be contained therein. Ammonia is added in an amount sufficient to subsequently dissolve the molybdenum and subsequently form the insoluble material. This procedure results in formation of magnesium ammonium arsenate and magnesium ammonium phosphate which precipitate and are present in the insoluble material.

Ammonia is added to the slurry in an amount sufficient to dissolve the molybdenum and to provide sufficient ammonium ions to subsequently form the magnesium ammonium arsenate and magnesium ammonium phosphate. The ammonia is added most typically in the form of ammonium hydroxide solution.

The sequence of addition of the components of the slurry can be varied. For example, the magnesium ions can be added either before or after the addition of the ammonia or together with the ammonia. However, when magnesium oxide, magnesium hydroxide, magnesium carbonate or combinations of these are used, it is preferred to add them to the acid slurry and thereafter to add the ammonia. The end result of precipitation of the magnesium ammonium arsenate and magnesium ammonium phosphate is the same.

The resulting ammoniated slurry is then digested at a temperature and time sufficient to dissolve the molybdenum and form the insoluble compounds while the pH is maintained at from about 9 to about 10 by addition of more ammonia as needed. The digestion temperature is usually about 55° C. and the time is about 2.5 hours.

As a result of the digestion, the molybdenum is converted to ammonium molybdate and the major portion of the arsenic and phosphorus are precipitated as their magnesium ammonium salts, which are magnesium ammonium arsenate and magnesium ammonium phosphate respectively.

The ammonium molybdate is separated from the digestion solids which contain the insoluble phosphorus and arsenic compounds, by standard techniques such as filtration.

The molybdenum can be recovered from the resulting ammonium molybdate by standard methods such as described in U.S. Pat. Nos. 4,604,266 and 4,525,331.

The arsenic content of the purified molybdenum compound is typically less than about 8 weight ppm and the phosphorus content is less than about 10 weight ppm.

Precipitation of P and As occurs by these equations:

    Mg.sup.+2 +NH.sub.4.sup.+ +PO.sub.4.sup.-3 →MgNH.sub.4 PO.sub.4

    Mg.sup.+2 +NH.sub.4.sup.+ +AsO.sub.4.sup.-3 →MgNH.sub.4 AsO.sub.4

Precipitation occurs when SOLUBILITY PRODUCT is exceeded. Precipitation does not occur unless SOLUBILITY PRODUCT IS exceeded.

K_(sp) is the symbol for SOLUBILITY PRODUCT

For MgNH₄ PO₄ : K_(sp) =[Mg⁺² ][NH₄ ⁺ ][PO₄ ⁻³ ]

For MgNH₄ AsO₄ : K_(sp) =[Mg⁺² ][NH₄ ⁺ ][AsO₄ ⁻³ ]

The [ ] means molar concentration, or moles per liter.

K_(sp) in practice can be very different than reported values, which usually pertain to aqueous solution.

K_(sp) for MgNH₄ PO₄ =2.5×10⁻¹³ (reported value)

K_(sp) for MgNH₄ PO₄ =4×10⁻⁷ (estimated from the present work)

K_(sp) for MgNH₄ AsO₄ =5×10⁻⁷ (estimated from the present work)

Equal weights of P and As in technical grade (impure) MoO₃ have different molarities in solution. They may not, therefore, precipitate to the same extent. Because [PO₄ ⁻³ ] is larger in size than [AsO₄ ⁻³ ], it may precipitate completely. Low [AsO₄ ⁻³ ] contributes to incomplete separation since K_(sp) for MgNH₄ AsO₄ may not be exceeded.

Different molarities from equal masses are shown in Table 1. It is based on 50 weight ppm P and As in technical grade molybdenum trioxide.

                  TABLE 1                                                          ______________________________________                                         Molarity Differences in Ammonium Molybdate (AM)                                From Equal Masses in MoO.sub.3                                                        ppm       concentration in AM                                                    in          (mass)   (molarity)                                       impurity MoO.sub.3   g/l      moles/l                                          ______________________________________                                         P        50          0.018    5.8 × 10.sup.-4                            As       50          0.018    2.4 × 10.sup.-4                            ______________________________________                                    

The following molarities are used in the following example of incomplete As precipitation.

    ______________________________________                                         species         moles/l                                                        ______________________________________                                         Mg.sup.+2       0.01                                                           NH.sub.4        1 (estimated, for pH 9.9)                                      PO4.sup.-3      5.8 × 10.sup.-4 (from Table 1)                           AsO.sub.4 -3    2.4 × 10.sup.-4 (from Table 1)                           ______________________________________                                    

The example is seen in Table 2 and is discussed below. In the example, MgNH₄ PO₄ is considered to precipitate before MgNH₄ AsO₄. The P and As are shown in Table 2 to precipitate in 10 weight ppm increments in Mo (or in 0.002 g/l units in AM having 200 g Mo/l). Each line in Table 2 represents another step in the precipitation.

                  TABLE 2                                                          ______________________________________                                         Illustration of Incomplete Arsenic Precipitation                               ______________________________________                                         .sup.K sp for MgNH.sub.4 PO.sub.4 = 4 × 10.sup.-7                                    Ppm P    mole  mole  mole                                          Line g P/l  in Mo    mg/l  NH.sub.4 /l                                                                          PO.sub.4.sup.-3 /l                                                                     Product                               ______________________________________                                          1   0.018  90       0.01  1     5.8 × 10.sup.-4                                                                  5.8 × 10.sup.-6                  2   0.016  80       0.0099                                                                               1     5.2 × 10.sup.-4                                                                  5.1 × 10.sup.-6                  3   0.014  70       0.0098                                                                               1     4.5 × 10.sup.-4                                                                  4.4 × 10.sup.-6                  4   0.012  60       0.00974                                                                              1     3.9 × 10.sup.-6                                                                  3.7 × 10.sup.-6                  5   0.010  50       0.00968                                                                              1     3.2 × 10.sup.-6                                                                  3.1 × 10.sup.-6                  6   0.008  40       0.00962                                                                              1     2.6 × 10.sup.-4                                                                  2.5 × 10.sup.-6                  7   0.006  30       0.00956                                                                              1     1.9 × 10.sup.-4                                                                  1.8 × 10.sup.-6                  8   0.004  20       0.00950                                                                              1     1.3 × 10.sup.-6                                                                  1.3 ×  10.sup.-6                In all of the above cases the Ksp is exceeded.                                 ______________________________________                                         .sup.K sp for MgNH.sub.4 AsO.sub.4 = 5 × 10.sup.-7                            g      ppm As   mole  mole  mole                                          Line As/l   in Mo    mg/l  NH.sub.4 /l                                                                          AsO.sub.4.sup.-3/l                                                                     Product                               ______________________________________                                          9   0.018  90       0.00950                                                                              1     2.4 × 10.sup.-4                                                                  2.3 × 10.sup.-6                 10   0.016  80       0.00947                                                                              1     2.1 × 10.sup.-4                                                                  2.0 × 10.sup.-6                 11   0.014  70       0.00941                                                                              1     1.9 × 10.sup.-4                                                                  1.8 × 10.sup.-6                 12   0.012  60       0.00941                                                                              1     1.6 × 10.sup.-6                                                                  1.5 × 10.sup.-6                 13   0.010  50       0.00938                                                                              1     1.3 × 10.sup.-6                                                                  1.2 × 10.sup.-6                 14   0.008  40       0.00935                                                                              1     1.1 × 10.sup.-4                                                                  9.8 × 10.sup.-7                 15   0.006  30       0.00932                                                                              1     7.8 × 10.sup.-5                                                                  7.2 × 10.sup.-7                 16   0.004  20       0.00929                                                                              1     5.2 × 10.sup.-5                                                                  4.8 × 10.sup.-7                 ______________________________________                                    

In all of the above cases, except for No. 16, the K_(sp) is exceeded.

Lines 1 through 8 in Table 2 describe MgNH₄ PO₄ precipitation. The column labeled "Product"=[Mg⁺² ]×[NH₄ ⁺ ]×[PO₄ ⁻³ ].

Lines 9 through 16 describe MgNH₄ AsO₄ precipitation. The column labeled "Product"=[Mg⁺² ]×[NH₄ ⁺ ]×[AsO₄ ⁻³ ].

In Line 1: "Product" exceeds K_(sp) and MgNH₄ PO₄ precipitates.

In Line 2 through 8: [Mg⁺² ] and [PO₄ ⁻³ ] become smaller as they are consumed in precpitation, but "Product" exceeds K_(sp) and MgNH₄ PO₄ precipitates. Phosphorus is quantitatively separated from Mo because K_(sp) is exceeded in all eight lines.

In line 9: Mg⁺² is <0.01 moles/l due to its use in MgNH₄ PO₄ precipitation. The starting [AsO₄ ⁻³ ] is only 2.4×10⁻⁴ moles/l. Nonetheless, "Product" exceeds K_(sp) and MgNH₄ AsO₄ precipitates.

In line 10 through 15: [Mg⁺² ] and [AsO₄ ⁻³ ] become smaller as they are consumed, but K_(sp) is exceeded and MgNH₄ AsO₄ precipitates.

In line 16: "Product" does not exceed K_(sp) and MgNH₄ AsO₄ does not precipitate. Arsenic is not quantitatively precipitated and it remains to contaminate the ammonium dimolybdate.

If line 16 has more Mg, MgNH₄ AsO₄ precipitation continues. If Mg is 0.014 moles/l, then "Product" is 7.8×10⁻⁷ which exceeds the K_(sp).

Assume that in Table 2 there is a line 17 in which As is 0.002 g/l. For K_(sp) to be exceeded, [Mg⁺² ] must be 0.019. Large excesses of Mg are needed to precipitate very small concentrations of arsenate.

Ammonium ion concentration is also critical. If [NH₄ ⁺ ] is 0.5, MgNH₄ AsO₄ precipitation ceases sooner, at line 14 when "Product" for MgNH₄ AsO₄ is 4.9×10⁻⁷. If [NH₄ ⁺ ] is 1.25, quantitative As separation occurs even at 0.00929 moles mg/l (line 16) since "Product" is 6×10⁻⁷.

To more fully illustrate the process steps of this invention, the following non-limiting examples are presented.

EXAMPLE 1

About 3 gallons of about 50% by weight hydrogen peroxide is added to an acid slurry of technical grade molybdenum trioxide to keep the Mo and any iron which might be present in their highest oxidation states. Ammonium hydroxide is added to dissolve the molybdenum trioxide and to provide NH₄ ⁺ ions. The resulting ammoniated slurry is stirred for about 30 minutes without heating after which it is heated to about 60° C. About 64 pounds of Mg(NO₃)₂.6H₂ O as a 1.5 molar solution is added. The resulting slurry is digested for about 2 hours at about 60° C. The magnesium ion concentration is about 0.02 moles/l. Ammonium hydroxide is added to maintain the pH at about 9.8 (measured at about 25° C.). The digested slurry is cooled to a about 35° C. and is filtered to remove the sludge from the molybdate solution. The sludge contains MgNH₄ AsO₄ and MgNH₄ PO₄. The phosphorus is reduced from about 50 weight ppm in the starting oxide to <10 weight ppm in the pure molybdenum trioxide which is produced from the above molybdate solution. Arsenic is reduced from about 50 weight ppm to less than a about 10 weight ppm in the pure molybdenum trioxide.

EXAMPLE 2

This example involves a series of tests to determine the effect of varying amounts of magnesium on the removal of As and P. Three test samples and a control are prepared as follows: about 100 g of technical grade molybdenum trioxide is stirred in about 400 ml of nitric acid-ammonium nitrate solution for about 2 hours at from about 75° to 85° C. The acid is decanted from the settled oxide. Water is added to restore the volume and the slurry is stirred for about 30 minutes at about 25° C. and water is decanted from the settled oxide. A second water wash is applied with agitation and the water is decanted off. The volume is adjusted with water, and about 3 ml of 50% by weight H₂ O₂ is added to each beaker. Ammonium hydroxide is added to dissolve the molybdenum trioxide and to maintain the pH at about 9.8. Aliquots of a 2M solution of MgCl₂.6H₂ O are added to provide 0.005, 0.01, and 0.015 moles Mg/l during the digestion. Magnesium is not added to the control. About a 30 minute digestion without heating precedes a 2 hour digestion at about 55° C., after which more ammonium hydroxide is added, if needed, to maintain the pH at about 9.8. Each sample is filtered after cooling to about 35° C. The compounds of MgNH₄ PO₄ and MgNH₄ AsO₄ are filtered out with the sludge. Each ammonium molybdate solution is converted to ammonium dimolybdate, which is then reduced to Mo metal. The Mo metal is analyzed spectrographically. The results are given in Table 3.

                  TABLE 3                                                          ______________________________________                                         As and P levels in Mo Metal                                                    versus moles Mg/l in NH4 .sup.OH Digestion                                                      Analysis of Mo metal                                                           weight ppm                                                    Moles Mg/l       As        P                                                   ______________________________________                                         0 Control        120       93                                                  0.005            85        63                                                  0.01             40        45                                                  0.015            45        26                                                  ______________________________________                                    

This data shows that the method is effective in lowering the P and As levels in the molybdenum, that P is more readily removed than As, and that As requires other conditions such as higher concentration of Mg for optimizing its removal.

EXAMPLE 3

Technical grade molybdenum trioxide is acid leached and water washed and ammonia is added as in Example 1. The slurry is stirred for about 30 minutes without heating before it is heated to about 55° C. A sample is taken as a control. To the balance of the slurry is added Mg(NO₃)₂.6H₂ O incrementally to determine the relationship between Mg concentration and degree of removal of the As and P. About 1M Mg(NO₃)₂.6H₂ O solution is added to provide 0.005 moles Mg/l, and the resulting slurry is digested for about 1 hour, and then a sample is taken. More of the 1M solution is added to provide 0.01 mole Mg/l, and a sample is taken after a digestion of about 1 hour. More of the 1M Mg solution is added to provide 0.02 moles Mg/l, and a sample is taken after a digestion of about 1 hour. More of the 1M Mg solution is added to provide 0.03 moles mg/l, and a sample is taken after a digestion of about 1 hour. Each of the sample solutions is filtered and allowed to stand. Precipitates formed in all but the control and they are removed from their respective solutions by filtration. Each ammonium molybdate sample solution is then converted to ammonium dimolybdate and then reduced to molybdenum for analysis. The results are given in Table 4.

                  TABLE 4                                                          ______________________________________                                         As and P levels in Mo Metal                                                    versus moles Mg/l in NH4 .sup.OH Digestion                                                      Analysis of Mo metal                                                           weight ppm                                                    Moles Mg/l       As        P                                                   ______________________________________                                         0 Control        21        >10                                                 0.005            14        >10                                                 0.01             20        >10                                                 0.02             12        >10                                                 0.03             >10       >10                                                 ______________________________________                                    

The data show that removal of arsenic is related to magnesium concentration. The higher the magnesium concentration, the more arsenic is removed.

EXAMPLE 4

About 5 kilograms of magnesium hydroxide are added to an acid slurry of 4500 pounds of technical grade molybdenum trioxide. This amount of magnesium is sufficient to result in a concentration of about 0.015 moles/l. About 3 gallons of 50% by weight H₂ O₂ are added to keep the Mo and Fe in their highest oxidation states. Ammonium hydroxide is added to dissolve the molybdenum trioxide and to provide NH₄ ⁺ ions. The resulting ammoniated slurry is agitated for about 30 minutes without heating after which it is heated to about 60° C. The resulting slurry is digested for abouat 2 hours at about 60° C. Ammonium hydroxide is added to maintain the pH at about 9.8 (measured at about 25° C.). The digested slurry is cooled to about 35° C. and is filtered to remove the sludge from the molybdate solution. The sludge contains MgNH₄ AsO₄ and MgNH₄ PO₄. The As and P contents which are each about 40 weight ppm in the starting technical grade molybdenum trioxide are lowered to less than 10 weight ppm in the resulting pure molybdemum trioxide.

While there has been shown and described what are at present considered the preferred embodiments of the invention, it will be obvious to those skilled in the art that various changes and modifications may be made therein without departing from the scope of the invention as defined by the appended claims. 

What is claimed is:
 1. In a process of purifying molybdenum containing arsenic and phosphorous during the preparation of ammonium molybdate consisting essentially of:(a) leaching molybdenum trioxide containing from about 1 to about 100 weight parts per million of phosphorus and from about 1 to about 120 weight parts per million of arsenic in nitric acid at a temperature of above about 70° C. to remove impurities from said molybdenum trioxide and produce a partially purified molybdenum trioxide; (b) adding to an acidic slurry of the resulting leached molybdenum trioxide, a source of magnesium ions in a solid form, with the amount of magnesium being sufficient to result in a magnesium ion concentration of from about 0.005 to about 0.04 moles Mg/l in the subsequently formed ammonium molybdate solution to subsequently form insoluble material containing greater than about 80% by weight of the arsenic and greater than about 80% by weight of the phosphorus, and ammonia in an amount sufficient to subsequently dissolve the molybdenum and subsequently form said insoluble compounds; (c) digesting the resulting ammoniated slurry at a pH of about 9 to about 10 at a temperature sufficient to dissolve the molybdenum and form an ammonium molybdate solution to form a solid containing said insoluble compounds; and (d) separating said solid from said ammonium molybdate solution.
 2. A process of claim 1 wherein the source of magnesium ions is selected from the group consisting of magnesium oxide, magnesium hydroxide, magnesium carbonate, magnesium nitrate, magnesium chloride, magnesium sulfate, and combinations of these.
 3. A process of claim 2 wherein said source of magnesium ions is selected from the group consisting of magnesium oxide, magnesium hydroxide, and combinations of these.
 4. A process of claim 3 wherein said source of magnesium ions is added to said acid slurry prior to the addition of ammonia. 